CL-SNF-18
| Proyék deteksi | Indéks kinerja | Nilai diukur | |
| Rasio pangurangan cai% | ≥14 | ≥20 | |
| Rasio laju perdarahan% | ≤90 | ≤80 | |
| Kandungan gas% | ≤3.0 | ≤2.0 | |
| Jurang waktos kondensasi (mnt) | Kondensasi awal | -90~120 | -90~120 |
| Kondensasi ahir | |||
| Rasio kakuatan compressive% | 1d | ≥140 | ≥160 |
| 3d | ≥130 | ≥150 | |
| 7d | ≥125 | ≥140 | |
| 28 d | ≥120 | ≥130 | |
| Babandingan laju shrinkage% | ≤135 | ≤135 | |
| Pangaruh korosi pikeun baja | Euweuh | Euweuh | |
| Indéks uniformity | Proyék deteksi | Indéks bubuk snf (SNF-C) | |
| Kandungan padet (%) | ≥92 | ||
| Kabugaran (%) | 0.315mm (sésa) <10 | ||
| nilai PH (10g/L) | 7--9 | ||
| Kandungan ion klorin(%) | ≤0.5 | ||
| eusi natrium sulfat (%) | ≤18 | ||
| Total eusi alkali(%) | ≤20 | ||
| Matéri teu leyur(%) | ≤0.5 | ||
| fluidity bersih semén (mm) | ≥220 | ||
| Penampilan | bubuk konéng-coklat | ||
Loba dipaké dina rékayasa beton, prefabricated, sleeper, sasak, torowongan, pertahanan nasional, rékayasa militér, conservancy cai, rékayasa kakuatan, terminal port, landasan bandara, rékayasa wangunan luhur-naékna.
Dosage:0,5% -1,5%, pamaké kudu nurutkeun kana kabutuhan ékspérimén pikeun nangtukeun dosage optimal.
Plastisitas anu luar biasa: Sacara statistik, kakuatan komprési dina dinten ka-1, dinten ka-3 sareng dinten ka-28 saatos aplikasi tunggal ningkat ku 60% -90% sareng 25% -60% masing-masing nalika ditambah dina dosis campuran standar.Hasilna, kakuatan komprési, kakuatan tensile, kakuatan buckling jeung modulus élastisitas bakal ningkat kana extent sababaraha.
Dina kaayaan rasio cai / semén sarua, collapsibility bisa ngaronjat 5-8 kali lamun ditambahkeun dina 0,75% dosage adun.
15-20% tina semén bisa ditangtayungan nalika agén ieu dicampurkeun dina 0,75% dosage adun, nu geus preconditioned ku collapsibility sarua jeung kakuatan.