Proyék deteksi | Indéks kinerja | Nilai diukur | |
Rasio pangurangan cai% | ≥14 | ≥20 | |
Rasio laju perdarahan% | ≤90 | ≤80 | |
Kandungan gas% | ≤3.0 | ≤2.0 | |
Jurang waktos kondensasi (mnt) | Kondensasi awal | -90~120 | -90~120 |
Kondensasi ahir | |||
Rasio kakuatan compressive% | 1d | ≥140 | ≥160 |
3d | ≥130 | ≥150 | |
7d | ≥125 | ≥140 | |
28 d | ≥120 | ≥130 | |
Babandingan laju shrinkage% | ≤135 | ≤135 | |
Pangaruh korosi pikeun baja | Euweuh | Euweuh | |
Indéks uniformity | Proyék deteksi | Indéks Bubuk snf (SNF-B) | |
Kandungan padet (%) | ≥92 | ||
Kabugaran (%) | 0.315mm (sésa) <10 | ||
nilai PH (10g/L) | 7--9 | ||
Kandungan ion klorin(%) | ≤0.5 | ||
eusi natrium sulfat (%) | ≤10 | ||
Total eusi alkali(%) | ≤20 | ||
Matéri teu leyur(%) | ≤0.5 | ||
fluidity bersih semén (mm) | ≥220 | ||
Penampilan | bubuk konéng-coklat |
Loba dipaké dina rékayasa beton, prefabricated, sleeper, sasak, torowongan, pertahanan nasional, rékayasa militér, conservancy cai, rékayasa kakuatan, terminal port, landasan bandara, rékayasa wangunan luhur-naékna.
Dosage:0,5% -1,0%, pangguna kedah dumasar kana kabutuhan ékspérimén pikeun nangtukeun dosis optimal.
Plastisitas Luar Biasa: Sacara statistik, kakuatan komprési dina dinten ka-1, dinten ka-3 sareng dinten ka-28 saatos aplikasi tunggal ningkat ku 60% -90% sareng 25% -50% masing-masing nalika ditambah dina dosis campuran standar.Hasilna, kakuatan komprési, kakuatan tensile, kakuatan buckling jeung modulus élastisitas bakal ningkat kana extent sababaraha.
Dina kaayaan rasio cai / semén sarua, collapsibility bisa ngaronjat 4-7 kali lamun ditambahkeun dina 0,75% dosage adun.
15-18% tina semén bisa ditangtayungan lamun agén ieu dicampurkeun dina 0,75% dosage adun, nu geus preconditioned ku collapsibility sarua jeung kakuatan.